Member Login English Home 中文版 日本語版 BBS Blog
Navigation
Home Page
Tungsten's News
Tungsten's News,International
Tungsten's News,China
Powder Metallurgy Technology
News of Molybdenum
News of Refractory Metals
History of Tungsten
Sports & Tungsten
Military & Tungsten
Environment & Tungsten
Radiation Medical & Tungsten
Marketing of Tungsten
Tungsten Ore
Tungsten Oxides & Trioxides
Tungsten、Carbide Powder
Pure Tungsten
Tungsten Welding Electrodes
Tungsten Heavy Alloy
Tungsten Copper
Tungsten Jewelry
Ferro Tungsten
Tungsten Carbides
Tungsten Alloy Darts
Scrap Tungsten
Tungsten Alloy Bucking Bars
Non-ferrous metals
Molybdenum Related
Nickel Related
Cobalt Related
Vanadium Related
Titanium Related
Rare Earth
Technology of tungsten
Acknowledge of tungsten
Academic of tungsten
Research & Development
Patented Technology
Information Services
Information Offer
Advertising
Translation Services
Agent & Representative
Magazines & Books of tungsten
Cobalt and Cobalt Alloys
Author:keytomet…    Source:keytometals    Update Time:2009-12-13 23:18:29

Cobalt and Cobalt Alloys


 

Cobalt and Cobalt Alloys


Abstract:
This article provides a general overview of cobalt-base alloys as wear-resistant, corrosion-resistant, and/or heat-resistant materials. Particular emphasis is placed on cobalt-base alloys for wear resistance, because this is the single largest application area of cobalt-base alloys.
Cobalt is useful in applications that utilize its magnetic properties, corrosion resistance, wear resistance, and/or its strength at elevated temperatures.

This article provides a general overview of cobalt-base alloys as wear-resistant, corrosion-resistant, and/or heat-resistant materials. Particular emphasis is placed on cobalt-base alloys for wear resistance, because this is the single largest application area of cobalt-base alloys. In heat-resistant applications, cobalt is more widely used as an alloying element in nickel-base alloys with cobalt tonnages in excess of those used in cobalt-base heat-resistant alloys.

Elemental Cobalt

Physical Properties. With an atomic number of 27, cobalt falls between iron and nickel on the periodic table. The density of cobalt is 8.8 g/cm3 similar to that of nickel. Its thermal expansion coefficient lies between those of iron and nickel. At temperatures below 417°C cobalt exhibits a hexagonal close-packed structure. Between 417°C and its melting point of 1493°C, cobalt has a face-centered cubic structure.

The elastic modulus of cobalt is about 210 GPa (30 x 106 psi) in tension and about 183 GPa (26.5 x 106 psi) in compression.

Uses of Cobalt. As well as forming the basis of the cobalt-base alloys discussed in this article, cobalt is also an important ingredient in other materials:

  • Paint pigments
  • Nickel-base superalloys
  • Cemented carbides and tool steels
  • Magnetic materials
  • Artificial g-ray sources
Of these applications, paint pigment represents the single largest use of cobalt.

In the nickel-base superalloys, cobalt (which is present typically in the range 10 to 15 wt%) provides solid solution strengthening and decreases the solubility of aluminum and titanium, thereby increasing the volume fraction of gamma prime (?,) precipitate.

The role of cobalt in cemented carbides is to provide a ductile bonding matrix for tungsten-carbide particles. The commercially significant cemented carbides contain cobalt in the range of 3 to 25 wt%. As cutting tool materials, cemented carbides with 3 to 12 wt% Co are commonly used.

Cobalt, which is naturally ferromagnetic, provides resistance to demagnetization in several groups of permanent magnet materials. These include the aluminum-nickel-cobalt alloys (in which cobalt ranges from about 5 to 35 wt%), the iron-cobalt alloys (approximately 5 to 12 wt%). and the cobalt rare-earth intermetallics (which have some of the highest magnetic properties of all known materials).

The artificial isotope cobalt-60 is an important ?-ray source in medical and industrial applications.

Cobalt-Base Alloys

As a group, the cobalt-base alloys may be generally described as wear resistant, corrosion resistant, and heat resistant (strong even at high temperatures).

As a group, the cobalt-base alloys may be generally described as wear resistant, corrosion resistant, and heat resistant (strong even at high temperatures). Many of the properties of the alloys arise from the crystallographic nature of cobalt (in particular its response to stress), the solid-solution-strengthening effects of chromium, tungsten, and molybdenum, the formation of metal carbides, and the corrosion resistance imparted by chromium. Generally the softer and tougher compositions are used for high-temperature applications such as gas-turbine vanes and buckets. The harder grades are used for resistance to wear.

Historically, many of the commercial cobalt-base alloys are derived from the cobalt-chromium-tungsten and cobalt-chromium-molybdenum ternaries first investigated by Elwood Haynes in the beginning of 20th century. He discovered the high strength and stainless nature of the binary cobalt-chromium alloy, and he later identified tungsten and molybdenum as powerful strengthening agents within the cobalt-chromium system. When he discovered these alloys, Haynes named them the Stellite alloys after the Latin stella (star), because of their star-like luster. Having discovered their high strength at elevated temperatures, Haynes also promoted the use of Stellite alloys as cutting tool materials.

Cobalt-Base Wear-Resistant Alloys

The cobalt-base wear alloys of today are little changed from the early alloys of Elwood Haynes. The most important differences relate to the control of carbon and silicon (which were imparities in the early alloys). Indeed, the main differences in the current Stellite alloy grades are carbon and tungsten contents (hence the amount and type of carbide formation in the microstructure during solidification). Carbon content influences hardness, ductility, and resistance to abrasive wear. Tungsten also plays an important role in these properties.

Chemical composition of Stellite alloys is approximately:

Cr ~ 25-30%
Mo = 1% max
W = 2-15%
C ~ 0.25-3.3%
Fe = 3% max
Ni = 3% max
Si = 2% max
Mn = 1% max.
Co = rest of balance

Types of wear. There are several distinct types of wear which generally fall into three main categories:

  • Abrasive wear
  • Sliding wear
  • Erosive wear.
The type of wear encountered in a particular application is an important factor that influences the selection of a wear-resistant material.

Abrasive wear is encountered when hard particles, or hard projections (on a counter-face) are forced against, and moved relative to a surface. The terms high and low stress abrasion relate to the condition of the abrasive medium (be it hard particles or projections) after interaction with the surface. If the abrasive medium is crushed, then the high stress condition is said to prevail. If the abrasive medium remains intact, the process is described as low stress abrasion. Typically, high stress abrasion results from the entrapment of hard particles between metallic surfaces (in relative motion), while low stress abrasion is encountered when moving surfaces come into contact with packed abrasives, such as soil and sand.

In alloys such as the cobalt-base wear alloys, which contain a hard phase, the abrasion resistance generally increases as the volume fraction of the hard phase increases. Abrasion resistance is, however, strongly influenced by the size and shape of the hard phase precipitates within the microstructure and the size and shape of the abrading species.

Sliding Wear. Of the three major types of wear, sliding is perhaps the most complex, not in concept, but in the way different materials respond to sliding conditions. Sliding wear is a possibility whenever two surfaces are forced together and moved relative to one another. The chances of damage are increased markedly if the two surfaces are metallic in nature, and if there is little or no lubrication present.

Cobalt-Base High-Temperature Alloys

For many years, the predominant user of high-temperature alloys was the gas turbine industry. In the case of aircraft gas turbines, the chief material requirements were elevated-temperature strength, resistance to thermal fatigue, and oxidation resistance. For land-base gas turbines, which typically burn lower grade fuels and operate at lower temperatures, sulfidation resistance was the major concern.

Today, the use of high-temperature alloys is more diversified, as more efficiency is sought from the burning of fossil fuels and waste, and as new chemical processing techniques are developed.

In general, cobalt-base high-temperature alloys have the following chemical composition:

Cr = 20-23%
W = 7-15%
Ni = 10-22%
Fe = 3% max
C = 0.1-0.6%
Co = rest of balance.

Although cobalt-base alloys are not as widely used as nickel and nickel-iron alloys in high-temperature applications, cobalt-base high-temperature alloys nevertheless play an important role, by virtue of their excellent resistance to sulfidation and their strength at temperatures exceeding those at which the gamma-prime- and gamma-double-prime-precipitates in the nickel and nickel-iron alloys dissolve. Cobalt is also used as an alloying element in many nickel-base high-temperature alloys.

Cobalt-Base Corrosion-Resistant Alloys

Although the cobalt-base wear-resistant alloys possess some resistance to aqueous corrosion, they are limited by grain boundary carbide precipitation, the lack of vital alloying elements in the matrix (after formation of the carbides or Laves precipitates) and, in the case of the cast and weld overlay materials, by chemical segregation in the microstructure.

By virtue of their homogeneous microstructures and lower carbon contents, the wrought cobalt-base high-temperature alloys (which typically contain tungsten rather than molybdenum) are even more resistant to aqueous corrosion, but still fall well short of the nickel-chromium-molybdenum alloys in corrosion performance.

To satisfy the industrial need for alloys which exhibit outstanding resistance to aqueous corrosion, yet share the attributes of cobalt as an alloy base (resistance to various forms of wear, and high strength over a wide range of temperatures), several low-carbon, wrought cobalt-nickel-chromium-molybdenum alloys are produced.

Chemical composition of these alloys is:

Cr = 20-25%
W = 2%
Mo = 5-10%
Ni = 9-35%
Fe = 3% max
C = 0.8% max
N = 0.1% max
Co = rest of balance.


If you need any more details of the above news and/or products, please visit Chinatungsten Online, or contact us directly.
Disclaimer: The article is only reflecting the opinions of the author. We have no responsibility to prove the originality and authenticity of the content, words and/or pictures. You readers should just take it as reference and check the details by yourselves. And the content is not a suggestion for investment decision. The investor takes his or her own risks if he or she operates accordingly. If you have any dissent about the contents above, please contact the relevant author, or the webmaster. We will try our best to assist the dealing of the related issues. Thanks for your visit and cooperation.

Article录入:hanns    责任编辑:hanns 
  • 上一itemArticle:

  • 下一itemArticle:
  • 【Font:Small Large】【发表评论】【加入收藏】【告诉好友】【打印此文】【关闭窗口
    Links
    China Tungsten Online Molybdenum Tungsten Wire Tungsten Bars/Rods Tungsten Bucking Bar
    Tungsten Carbides Tungsten Heater Pure Tungsten Tungsten Carbide & Alloy Tungsten Paper weight
    Tungsten Heavy Alloy Tungsten Powder China Dart Wiki of WMo Infosys
    Darts Shop Online f2f.com.cn Xatcm Global InfoMine Stainless Steel Rails
    Sheet Metal Machinery Interactive Investor Link Exchange

    Add to FavoriteAbout CTIAContact UsMore LinksRecruitmentBusiness

    Address: 2-27B,No.261-265 Jiahe RD,Xiamen,Fujian 361009 P.R.China
    Phone:+86 592-5129696,+86 592-5129595;Fax:+86 592-5129797
    Sponsors: China Tungsten Industry Association,Chinatungsten Online
     Certified by MIIT:闽B2-20090025 闽ICP备05002525号
    Copyright © 2000 - 2009 Chinatungsten Online All Rights Reserved