[Nickel]:Spheroidization of graphite and properties of new Ni-Cu-C alloy
The Ni-Cu-C solid self-lubricating materials were prepared by melting method and the spheroidization effect of rare earth magnesium on graphite of Ni-Cu-C was studied. The results show that with the addition percent of Cu within 050%, the spheroidization effect of 0.75% of rare earth magnesium on the graphite during crystallization is effective. After the graphite being spheroidized, its nucleation density increases and distributes homogeneously. The solution of Cu improves the hardness of alloy matrix and the electrical resistivity of Ni-Cu- C alloy. The more adding of Cu has the effective spheroidization on the graphite, but reduces the content graphite. The self-lubricating properties of Ni-Cu-C alloy increase with the increasing of graphite content and spheroidization. Through dry friction and wear experiment against 45# annealed steel and GCr15 bearing steel, it was found that the friction coefficient of the Ni-20%Cu-3.5%C alloy remains stably as 0.12 and 0.13, respectively.....Details,please contact the auther, editor directly.
采用熔炼法制备出新型Ni Cu C固体自润滑材料,研究了稀土镁球化剂对Ni Cu C合金中石墨的球化作用。结果表明:在加入铜量0~50%范围内,用0.75%的稀土镁球化剂可以使结晶的石墨有效球化;石墨经球化处理后,形核密度提高,分布均匀;铜的固溶作用提高了合金基体的硬度,增大了材料的电阻率,在加入量大的情况下,对石墨有一定的球化作用,但降低石墨的含量;Ni Cu C合金的自润滑性能随石墨含量的提高及球化而得到改善;与退火态45#钢和GCr15轴承钢进行干摩擦磨损时,Ni 20%Cu 3.5%C合金的摩擦因数分别保持在0.12和0.13。
【Key words】 Ni-Cu-C alloy; melting method; rare earth magnesium nodularizer; spheroidization; friction and wear
【关键词】 niCuC合金; 熔炼法; 稀土镁球化剂; 球化处理; 摩擦磨损 If you need any more details of the above news and/or products, please visit Chinatungsten Online, or contact us directly.
Disclaimer: The article is only reflecting the opinions of the author. We have no responsibility to prove the originality and authenticity of the content, words and/or pictures. You readers should just take it as reference and check the details by yourselves. And the content is not a suggestion for investment decision. The investor takes his or her own risks if he or she operates accordingly. If you have any dissent about the contents above, please contact the relevant author, or the webmaster. We will try our best to assist the dealing of the related issues. Thanks for your visit and cooperation.
|