[Nickel]:Sol-gel Method Preparation and Characterization of NiMoO_4 Ultrafine Particle Catalyst
Ni Mo ultrafine particle samples have been prepared by sol gel method with citric acid as complexant. DTA, BET, XRD and LRS have been employed to characterize the structures of the samples obtained by calcining the Ni Mo gel at various temperatures. The results show that when the Ni Mo gel is calcined in air at 210 ℃, citric acid reacts violently with O2, it produces a flash heat and results in an aggregation of the Ni Mo particles. When the gel is calcined in argon,citric acid is removed mildly and NiMoO4 ultrafine particles are formed.After calcined at 500 ℃, the ultrafine particles grow up with a decrease of BET surface area from 51.5 m2·g-1 to 25.0 m2·g-1.....Details,please contact the auther, editor directly.
以柠檬酸为络合剂,采用溶胶凝胶法制备NiMoO4超细粒子催化剂.使用DTA、BET比表面测定、XRD和LRS等表征手段考察了热处理条件和焙烧温度对粒子结构的影响.结果表明,在氩气气氛中于210℃分解干凝胶中的柠檬酸,可以避免柠檬酸分解时燃烧大量放热而引起超细微粒的烧结,脱除柠檬酸后的超细粉末为NiMoO4.经400℃以上的高温处理后,微粒明显晶化. If you need any more details of the above news and/or products, please visit Chinatungsten Online, or contact us directly.
Disclaimer: The article is only reflecting the opinions of the author. We have no responsibility to prove the originality and authenticity of the content, words and/or pictures. You readers should just take it as reference and check the details by yourselves. And the content is not a suggestion for investment decision. The investor takes his or her own risks if he or she operates accordingly. If you have any dissent about the contents above, please contact the relevant author, or the webmaster. We will try our best to assist the dealing of the related issues. Thanks for your visit and cooperation.
|